Galerie de L'Ancienne Poste

As the wind howls fiercely across the country I feel lucky to have chosen to drive to France and back using the Tunnel rather than ferry.

Last week I packed up the car with work from the last two firings and drove down to Toucy, south of Paris, to deliver work to the Galerie de L'Ancienne Poste for my solo exhibition there. The work was set up for the opening on Saturday giving me time to explore the beautiful town.

We were staying in a gite overlooking the south of the town and the impressive church at its centre, amid narrow cobbled streets and some beautiful old buildings. The local patisseries and cafes gave me far too much opportunity to realise how much French I have forgotten through years of lack of use. I spent much time scrabbling through a ridiculously small English/French phrasebook trying to decipher menus and simple conversation, resolving to re-learn the language.

Our hosts, Isabelle and Christophe, were extremely hospitable and it was a real pleasure having time to dine and talk with them - luckily (and embarrassingly) their English was far better than my French!
The opening was on Saturday evening, which went very well. It was good to meet some of the new owners of my work and see their reaction to the exhibition.

I took these photos on the Sunday morning at 10am just before the long trip home.
If you live near to Toucy or are visiting France, please go along to the gallery. It shows great examples of my work and it's so much better to see it in the flesh than in photos.

Who would have thought.......

....that dinosaur dung could look so good?
The testing stage that I've been carrying out on this unusual material is over and I have a range of glazes for different parts of the wood kiln.

This test tile shows a series of lineblends fired in my gas kiln to cone 10, where I managed to get the refractory coprolite to melt into a glaze. It's coloured the glaze green due to its iron content, but seems to have added little to the character of the glazes in these tests. I was happy with these tests as I finally managed to get the coprolite to melt, rather than just sit suspended in the glaze.
Last week I fired my wood kiln and dotted test pots around the kiln with four test glazes selected from this tile.

I'll upload a few images of these little pots, which gave quite varied but rather beautiful results. There were good ash deposits throughout the kiln, but there are also quite distinct areas within the pack - each with its own characteristics. All of the glazes selected gave good results in at least one of these areas, but not all.

This is how I usually test my glazes, so that I can plan the pack carefully and use specific glazes for particular places within the kiln.
Now I'm ready to glaze the final pieces and fire them in the smaller wood kiln.

Schrodinger's cat

All possibilities are present within an unopened kiln: every success, disaster, mistake, fault or beauty: a superposition of states. At last, once well cool, the kiln door was unbricked, the wave functions collapse and I can see what reality has decided. Is the cat alive or dead?

Now, a day later, when most crazing and possible dunting has occurred, I can see that the cat is alive. Not merely alive - it's running round the workshop doing tricks! Impending disaster precluded, it looks as if it was one of my very best firings.
this view is through the stoke hole into the first stack. As you can see cone 12 as well as safety 15 is still standing, indicating a cooler front than usual.
There is some heavy crystallisation on the surfaces here, which is mostly welcome.

The sidestoke area was, as usual, the hottest, and I got some really stunning pieces from the parts of the stack facing this area. In gas kiln tests the glazes that I have developed are often rather stiff, fat and uninteresting. I'm hoping that the ash and volatiles from the firing are really going to effect them, creating variation in colour and texture, and really pull some beauty out of them. This piece has a white silica rich glaze from Edinburgh rocks. I love it when it breaks to watery electric blues like this.

Many of the pieces I made for this firing were carved, exposing the structure of the clays I am using. This bowl shows the variation of colour I managed to get throughout the kiln, and the quality of the coarse clay.
The photos are just quick snaps outside the workshop as I begin the grinding process. I will post properly done ones soon.
As usual, there were some disappointing results, especially so with pieces that took hours and hours to make, but there is a broad range of spectacular colour and textures. I seem to have managed to reduce the tendency of glazes to peel off pots during the early stages of the firing, but other faults are rearing their ugly heads. It is particularly hard woodfiring heavily glazed pots in an ash rich firing, on found clays  (it's stressful on both the potter and the pots), but the occassional flashes of brilliance make it impossible to give up. The new fault is in small areas on pots, where ash runs form sugary matt surfaces on cooling, but appaer to contract slightly less than the glaze layer/clay below them, and start to look a little like crazy paving, with rough edges. It often seems to happen on the vesry best pieces so is a serious problem. Any advice welcomed!

The long slow cool

After a day of torrential rain and the gales blowing today there was a (fortuitous rather than anticipated) window of rather gentle dry and often sunny weather, where the beginnings of Spring can be felt pushing through the hard shell of winter. What a great time to fire the kiln!

Andy came over to help (taking holiday from his full time job - thanks Andy) and on the first day Brigitte (who helps Svend Bayer fire his kilns) came up to the edge of the Fens as well.
On the whole it was a pretty cruisy first day - lit at 7am, red heat starting at the front at noon and kicking into reduction at 3pm. Once reduction is settled I aim for a good steady rise in temperature till cone 8's start going down throughout the kiln.
It is soaked overnight at this temperature, and typically cone 9's and cone 10's slowly tip during these shifts. The firebox area is not that big and, when the fire and embers are up close to the stack, the front tends to be a little cooler than the rear chamber. That was certainly the case this time, with cone 8 still not quite over at the front by 8am. Sidestoking is only to build up an ember bed mid-kiln and care must be taken not to heat up the back chamber too much.

Nudging the kiln back into a gentle temperature rise involves coaxing a heat build up in the front firebox until the wood starts crackling and the whole kiln seems to liven up. Six hours later and the temperature has risen by about 50 - 60C and cones 12 are down at the top and bottom of the back chamber. Despite my nerves cone 11 is well over at the front and cone 12 has started tipping. This seems quite acceptable. I quite like the very front being a little cooler than the rest as I often get some beautiful crystallisation and satin surfaces here. Back on to gentle stoking with small wood, right up the front of the kiln to keep the embers away from the stack, a one hours soak and it's a progressive clamming up, aiming to keep smoking to a minimum.

I love that time just after a firing, when it seems to have gone well and all the correct cones are down. It seems wrong to leave the kiln alone, so time for a few celebratory beers to toast the firing and to talk about the firing and pots in general.
The next morning it's still red hot inside the kiln + with aching muscles I braced the rising wind to walk the local fens. The long wait has started.